Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | | 0.1 | % |
Modeling Shrinkage | Across Flow | | 0.75 | % |
Modeling Shrinkage | Across Flow | | 0.16 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | | | 7 | kJ/m² |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 9 | KJ/m |
Tensile Strength | | ISO 527-1/-2 | 100 | Mpa |
Tensile Elongation | Break | | 2.5 | % |
Tensile Elongation | Break | ISO 527-1/- 2 | 2.2 | % |
Flexural Strength | | ISO 178 | 183 | Mpa |
Flexural Strength | | ISO 178 | 151 | Mpa |
Charpy Unnotched Impact Strength | 23℃ | ISO 179/1eU | 59 | KJ/m |
Charpy Unnotched Impact Strength | 23 ℃ | | 55 | kJ/m² |
Ball Indentation Hardness | | ISO 2039-1 | 164 | Mpa |
Ball Indentation Hardness | | ISO 2039-1 | 153 | Mpa |
Tensile Modulus | | | 9700 | Mpa |
Tensile Modulus | | ISO 527-1/-2 | 6900 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | | ISO 11359-1/-2 | 0.4 | E-4/°C |
Deflection Temperature Under Load? | 1.80 MPa | | 160 | °C |
Deflection Temperature Under Load? | 1.80 MPa | ISO 75-1/-2 | 175 | °C |
Deflection Temperature Under Load? | 0.45 MPa | ISO 75-1/-2 | 210 | °C |
Flammability | | UL94 | HB | |
Flammability | | UL94 | HB | |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Melt Temperature | | | 250-275 | °C |
Melt Temperature | | | 250-270 | °C |
Mold Temperature | | | 60-100 | °C |
Mold Temperature | | | 60-100 | °C |
Other | Test Condition | Test Method | Test Result | Unit |
---|
glass fiber content | | | 20 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | | 0.4 | % |
Moisture Absorption | | | 0.4 | % |
Density | | ISO 1183 | 1.39 | g/cm³ |
Density | | ISO 1183 | 1.47 | g/cm |
Melt index | | ISO 1133 | 20 | cm3/10min |
Melt index | | ISO 1133 | 20 | cm ³ /10min |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
glass fiber content | | | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.