PBT/ASA Ultradur® S 4090 G4 BK BASF GERMANY

177

Unit Price:
$4225 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low warpage Dimensional stability
Application Areas:Connector As for the load-bearing p Applied in fields that re
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTMD792	1.39	g/cm³
Density	Density		ISO1183	1.39	g/cm³
Melt Volume flow Rate	275°C/2.16kg	ISO1133	20.0	cm3/10min
Modeling Shrinkage	TD	ISO294-4	0.74	%
parent Viscosity	降低的粘度	ISO1628	105.0	ml/g
Modeling Shrinkage	MD	ISO294-4	0.43	%
Moisture Absorption	饱和	ASTMD570	0.40	%
	Moisture Absorption	饱和,23°C	ISO62	0.40	%
		Moisture Absorption	平衡,50%RH	ASTMD570	0.20	%
		Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	0.20	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	断裂,150°C	ISO527-2	32.2	Mpa
Tensile Elongation	断裂,23°C	ASTMD638	2.5	%
Tensile Strain	断裂,-40°C	ISO527-2	2.7	%
	Tensile Strain	断裂,23°C	ISO527-2	2.5	%
		Tensile Strain	断裂,80°C	ISO527-2	4.2	%
			Tensile Strain	断裂,120°C	ISO527-2	7.4	%
			Tensile Strain	Tensile Strain	断裂,150°C	ISO527-2	6.7	%
Tensile Modulus	23°C	ISO527-2	6900	Mpa
Tensile Strength	断裂,23°C	ASTMD638	100	Mpa
Tensile Stress	断裂,-40°C	ISO527-2	160	Mpa
	Tensile Stress	断裂,23°C	ISO527-2	100	Mpa
		Tensile Stress	断裂,80°C	ISO527-2	68.0	Mpa
		Tensile Stress	Tensile Stress	断裂,120°C	ISO527-2	42.0	Mpa
Tensile Creep Modulus	1hr	ISO899-1	5300	Mpa
Tensile Creep Modulus	1000hr	ISO899-1	4700	Mpa
Flexural Modulus	23°C	ASTMD790	6100	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	6400	Mpa
Flexural Strength	23°C	ASTMD790	159	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTIElec	3.0mm	UL746	130	°C
Evolution Calendar intelligent importer	0.71mm	UL746	90.0	°C
Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	1.5mm	UL746	90.0	°C
Deflection Temperature Under Load?	1.8MPa,未退火	ASTMD648	194	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	160	°C
Peak Melting Temperature		ASTMD3418	223	°C
Melting temperature (DSC)		ISO3146	223	°C
RTIElec	0.71mm	UL746	130	°C
RTIElec	RTIElec	1.5mm	UL746	130	°C
Evolution Calendar intelligent importer	3.0mm	UL746	90.0	°C
RTIStr	0.71mm	UL746	130	°C
	RTIStr	1.5mm	UL746	130	°C
	RTIStr	RTIStr	3.0mm	UL746	130	°C
Deflection Temperature Under Load?	0.45MPa,未退火	ASTMD648	216	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa,未退火	ISO75-2/B	205	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC60112	450	V
Surface Resistivity		ASTMD257	1E+14	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+14	ohms
Volume Resistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Volume Resistivity		IEC60093	>1.0E+13	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179	7.0	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179	43	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179	55	kJ/m²
Notched Izod Impact Strength	-40°C	ASTMD256	68	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	80	J/m
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180	7.0	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.