Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr | ISO62 | 0.40 | % |
Moisture Absorption | 23°C,50RH | ISO62 | 0.20 | % |
Density | | ISO1183 | 1.31 | g/cm³ |
Melt Mass-Flow Rate | 275℃/2.16Kg | ISO1133 | 35 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 37 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 24 | kJ/m² |
Tensile Elongation?(Break) | 23°C | ISO527-2 | 2.9 | % |
Tensile Modulus | 23°C | ISO527-2 | 4500 | Mpa |
Tensile Strength | 23°C | ISO527-2 | 75 | Mpa |
Flexural Strength | 23°C | ISO178 | 119 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
Tensile Creep Modulus | 1000Hr | ISO899-1 | 3300 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | ISO11357-3 | 223 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 5.5E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa未退火 | ISO75-2/Bf | 190 | °C |
Deflection Temperature Under Load? | 1.80MPa未退火 | ISO75-2/Af | 105 | °C |
Thermal Conductivity | | DIN52612 | 0.27 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface resistance | | IEC60093 | 1E+14 | Ω.cm |
Dielectric Constant | 23°C | IEC60250 | 3.60 | 100HZ |
Dielectric Constant | 23°C | IEC60250 | 3.40 | 1MHz |
Insulation strength | 1.50mm | IEC60243-1 | 22 | KV/mm |
Volume Resistivity | | IEC60093 | 1E+14 | Ω.cm |
Dissipation Factor? | 23°C | IEC60250 | 3.1E-03 | 100HZ |
Dissipation Factor? | 23°C | IEC60250 | 0.021 | 1MHz |
Flame retardancy | Test Condition | Test Method | Test Result | Unit |
---|
Fire rating | Allcolor | UL-94 | 0.71mm | HB |
Fire rating | Allcolor | UL-94 | 1.50mm | HB |
Fire rating | Allcolor | UL-94 | 3.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.