PA/MXD6 IXEF® 1524-9008 SOLVAY USA
189
- Unit Price:
- $10116 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 37MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 50% filler by weight
- Application Areas:Phone Shell
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.10to0.30 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.30 | % |
| Equilibrium,50%RH | 内部方法 | 1.0 | % | |
| Equilibrium,65%RH | 内部方法 | 1.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 20000 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 230 | Mpa |
| Tensile strain | Break | ISO527-2 | 1.9 | % |
| Bending modulus | ISO178 | 18500 | Mpa | |
| Bending stress | ISO178 | 330 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 227 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| DielectricConstant2 | 2.40GHz | ASTMD2520 | 4.44 | |
| DissipationFactor2 | 2.40GHz | ASTMD2520 | 0.012 | |
| Compared to the anti leakage trace index | 3.00mm | UL746 | >600 | V |
| 3.00mm | UL746 | PLC0 | ||
| Leakage Trace Index | IEC60112 | >600 | V | |
| High arc combustion index (HAI) | 0.400mm | UL746 | 37.6 | |
| 0.750mm | UL746 | 53.6 | ||
| 1.50mm | UL746 | 70.2 | ||
| 3.00mm | UL746 | 95.4 | ||
| 0.40mm | UL746 | PLC2 | ||
| 0.75mm | UL746 | PLC2 | ||
| 1.5mm | UL746 | PLC1 | ||
| 3.0mm | UL746 | PLC1 | ||
| High voltage arc tracing rate | 3.00mm | UL746 | PLC0 | |
| Hot wire ignition (HWI) | 0.400mm | UL746 | 95 | sec |
| 0.750mm | UL746 | >120 | sec | |
| 1.50mm | UL746 | >120 | sec | |
| 3.00mm | UL746 | >120 | sec | |
| 0.40mm | UL746 | PLC1 | ||
| 0.75mm | UL746 | PLC0 | ||
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179/1eU | 48 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating3 | 0.40mm,ALL | UL94 | V-0 | |
| Hot filament ignition temperature | 0.40mm | IEC60695-2-13 | 775 | °C |
| 0.75mm | IEC60695-2-13 | 800 | °C | |
| 1.5mm | IEC60695-2-13 | 825 | °C | |
| 3.0mm | IEC60695-2-13 | 850 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 37 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.