Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | 内部方法 | 0.10to0.30 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.30 | % |
Moisture Absorption | Equilibrium,50%RH | 内部方法 | 1.0 | % |
Moisture Absorption | Equilibrium,65%RH | 内部方法 | 1.3 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2 | 230 | Mpa |
Tensile Strain | Break | ISO527-2 | 1.9 | % |
Tensile Modulus | | ISO527-2 | 20000 | Mpa |
Flexural Modulus | | ISO178 | 18500 | Mpa |
Flexural Stress | | ISO178 | 330 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 227 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 2.40GHz | ASTMD2520 | 4.44 | |
DissipationFactor2 | 2.40GHz | ASTMD2520 | 0.012 | |
High Voltage Arc Tracking Rate | 3.00mm | UL746 | PLC0 | |
Comparative Tracking Index | | IEC60112 | >600 | V |
Comparative Tracking Index | 3.00mm | UL746 | >600 | V |
Comparative Tracking Index | 3.00mm | UL746 | PLC0 | |
High Amp Arc Ignition | 0.400mm | UL746 | 37.6 | |
High Amp Arc Ignition | 0.750mm | UL746 | 53.6 | |
High Amp Arc Ignition | 1.50mm | UL746 | 70.2 | |
High Amp Arc Ignition | 3.00mm | UL746 | 95.4 | |
High Amp Arc Ignition | 0.40mm | UL746 | PLC2 | |
High Amp Arc Ignition | 0.75mm | UL746 | PLC2 | |
High Amp Arc Ignition | 1.5mm | UL746 | PLC1 | |
High Amp Arc Ignition | 3.0mm | UL746 | PLC1 | |
Hot-wire Ignition | 0.400mm | UL746 | 95 | sec |
Hot-wire Ignition | 0.750mm | UL746 | >120 | sec |
Hot-wire Ignition | 1.50mm | UL746 | >120 | sec |
Hot-wire Ignition | 3.00mm | UL746 | >120 | sec |
Hot-wire Ignition | 0.40mm | UL746 | PLC1 | |
Hot-wire Ignition | 0.75mm | UL746 | PLC0 | |
Hot-wire Ignition | 1.5mm | UL746 | PLC0 | |
Hot-wire Ignition | 3.0mm | UL746 | PLC0 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179/1eU | 48 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 37 | % |
Glow Wire Ignition Temperature | 0.40mm | IEC60695-2-13 | 775 | °C |
Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 800 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 825 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 850 | °C |
Flame Rating | 0.40mm,ALL | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.