PARA IXEF® 1622/9003 SOLVAY USA

Unit Price:
$8465 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
44MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	275°C/2.16kg	g/10min	3.6到20
Melt Volume flow Rate	275°C/2.16kg	ISO 527-2/5, ISO 527-2/50	0.01到0.04
Saturation ,23℃		%	0.060到0.15
Flow,23℃,50%RH		%	0.70到1.5
--			1.36到1.82
23℃		%	0.19到0.40
23℃	23℃		g/cm³	1.43到1.77
23℃,24hr		%	0.16到0.30
Flow:23℃		mm/mm	38.1E-3到78.7E-3

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
23℃		MPa	280.0到402.07
	23℃		MPa	11931.03到24896.55
		23℃		MPa	7586.21到23448.28
			23℃		MPa	8482.76到21379.31
				23℃		MPa	141.38到268.97
					23℃		MPa	11517.24到23517.24
					23℃	23℃		MPa	203.45到389.66
Break,23℃		%	1.6到2.1
Break,23℃	Break,23℃		MPa	151.72到280.69
Yield,23℃		%	2.0到3.0

Thermal Properties	Test Method	Test Result
Flow	mm/mm/°C	55.9E-5到50.8E-5
Flow	mm/mm/°C	137.2E-5到25.4E-5
0.45MPa, Unannealed	°C	234到255
1.8MPa, Unannealed	°C	223到230

Electrical performance	Test Condition	Test Method	Test Result
Dielectric Strength	23℃	V/mil	500到840
Comparative Tracking Index		V	320到600
Surface Resistivity		ohms	5.0E+3到6.0E+15
Volume Resistivity	23℃	ohms·cm	3.0E+2到2.1E+16

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23℃	kJ/m²	2.647到20.893
Unnotched Izod Impact Strength	23℃	J/m	0.222到0.332

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Ignition Temperature		°C	798到904

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.