Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | 内部方法 | 0.10to0.30 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.15 | % |
Modeling Shrinkage (Equil,65%RH) | | 内部方法 | 1.3 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 230 | Mpa |
Tensile Strain | Break | ISO527-2 | 1.9 | % |
Tensile Modulus | | ISO527-2 | 20000 | Mpa |
Flexural Modulus | | ISO178 | 20000 | Mpa |
Flexural Stress | 23°C | ISO178 | 340 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 230 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.7E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 110Hz | IEC60250 | 4.10 | |
Volume Resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
Dissipation Factor? | 110Hz | IEC60250 | 0.012 | |
Dielectric Strength | | IEC60243-1 | 29 | KV/mm |
Comparative Tracking Index | | IEC60112 | 400 | V |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.75mm,Black2 | UL94 | V-0 | |
UL flame retardant rating | 1.5mm,ALL | UL94 | V-0 | |
UL flame retardant rating | 1.5mm,Black | UL94 | 5VA | |
Glow Wire Flammability Index | 0.8mm | IEC60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
Oxygen Index | | ISO4589-2 | 32 | % |
Glow Wire Ignition Temperature | 0.8mm | IEC60695-2-13 | 900 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 930 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 900 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.