Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow | ISO 294 | 0.2 | % |
| Modeling Shrinkage | 垂直 | ISO 294 | 0.4 | % |
| Moisture Absorption | 23°C 24hr | ISO 62 | 0.22 | % |
| proportion | | ISO 1183 | 1.51 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23℃ | ISO 180 | （60干态）(50湿态） | kJ/m² |
| Unnotched Izod Impact Strength | | ISO 180 | （370干态)(345湿态） | kJ/m² |
| Tensile Modulus | 23℃ | ISO 527 | （10000干态）(23000湿态） | Mpa |
| Tensile Strength | 23℃ | ISO 527 | （135干态）(190湿态） | Mpa |
| Tensile Elongation | 23℃ | ISO 527 | （2.2干态）(1.3湿态） | % |
| Flexural Modulus | 23℃ | ISO 178 | （8000干态）(21000湿态） | Mpa |
| Flexural Strength | 23℃ | ISO 178 | （215干态）(270湿态） | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | Unannealed1.8MPa | ISO 75 | 220 | °C |
| Melting temperature | | ISO 11357 | 280 | °C |
| Coefficient of Linear Thermal Expansion | Flow | ISO 11359 | 0.0029 | cm/cm/℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | 1000000000000000 | Ω.cm |
| Insulation Resistance | | IEC 60243 | 28 | KV/mm |
| Dielectric Constant | 110Hz | IEC 60250 | 3.9 | |
| Dissipation Factor? | 110Hz | IEC 60250 | 600 | V |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO 4589 | 23 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.