PBT/PET Pocan® T7331 LANXESS GERMANY

180

Unit Price:
$2149 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:270°C,2.00mm2	ISO294-4	0.90	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO294-4	0.20	%
		Shrinkage rate	MD:270°C,2.00mm2	ISO294-4	0.30	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO294-4	0.10	%
Water absorption rate	Saturation,23°C	ISO62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.10	%
Apparent density		ISO60	0.80	g/cm³
Melt volume flow rate	260°C/5.0kg	ISO1133	30.0	cm3/10min
Viscosity value	降低的粘度	ISO1628	91.0	ml/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending strain 5	23°C		3.0	%
Tensile strength	Break,23°C	ASTMD638	123	Mpa
Bending stress 4	23°C	ISO178	230	Mpa
Bending modulus 4	23°C	ISO178/A	10300	Mpa
Tensile stress	Break,23°C	ISO527-2/5	145	Mpa
Tensile strain	Break,23°C	ISO527-2/5	2.8	%
TensileCreepModule	1hr	ISO899-1	10000	Mpa
Tensile creep modulus	1000hr	ISO899-1	8500	Mpa
Tensile modulus	23°C	ASTMD638	9980	Mpa
Tensile modulus	Tensile modulus	23°C	ISO527-2/1	10400	Mpa
elongation	Break,23°C	ASTMD638	2.5	%
Bending modulus	23°C	ASTMD790	8550	Mpa
bending strength	23°C	ASTMD790	207	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	200	°C
RTIElec		UL746	140	°C
Evolution Calendar intelligent importer		UL746	125	°C
RTIStr		UL746	140	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6E-05	cm/cm/°C
Vicat softening temperature		ISO306/B120	205	°C
thermal conductivity	23°C	ISO8302	0.27	W/m/K
Melting temperature 7		ISO11357-3	225to250	°C
TemperatureIndex11	介电强度	IEC60216	155
	TemperatureIndex11	拉伸冲击强度	IEC60216	140
	TemperatureIndex11	TemperatureIndex11	抗张强度	IEC60216	155
Half Interval	--8	IEC60216	13.5	°C
	Half Interval	--9	IEC60216	10.2	°C
	Half Interval	Half Interval	--10	IEC60216	10.2	°C
BallPressure Test	220°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	23°C,100Hz	IEC60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	3.80
Leakage Trace Index	SolutionA	IEC60112	250	V
Dielectric strength	23°C,1.00mm	IEC60243-1	27	KV/mm

film	Test Condition	Test Method	Test Result	Unit
FilmPunctureEnergy6		ISO6603-2	2.10	J
Membrane piercing force 6		ISO6603-2	650	N

Impact performance	Test Condition	Test Method	Test Result	Unit
Unscented Izod impact strength	-30°C	ISO180/1U	55	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	55	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	65	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	200	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index 12		ISO4589-2	21	%
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL94	HB
Burning wire flammability index	2.0mm	IEC60695-2-12	750	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion		IEC60426	A1
ISO Shortcut		ISO7792	PBT+PET,GHLMR,09-100,GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.