PPO/PA NORYL GTX™ GTX4610-1710 SABIC INNOVATIVE US
183
- Unit Price:
- $6029 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance High temperature resistan Dimensional stability High mobility
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:Flame retardant and high temperature resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.88到0.94 | % |
| TD:3.20mm | 内部方法 | 0.95到1.0 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 3.8 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.50 | % | |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 18 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | --6,7 | ISO178 | 145 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 145 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 3.0 | % |
| Break | ISO527-2/5 | 3.0 | % | |
| Tensile Modulus | --3 | ASTMD638 | 5000 | Mpa |
| -- | ISO527-2/1 | 5000 | Mpa | |
| Flexural Modulus | 50.0mmSpan5 | ASTMD790 | 4600 | Mpa |
| --6 | ISO178 | 4600 | Mpa | |
| Tensile Strength | Yield | ISO527-2/5 | 88.0 | Mpa |
| Break4 | ASTMD638 | 88.0 | Mpa | |
| Break | ISO527-2/5 | 88.0 | Mpa | |
| Yield4 | ASTMD638 | 88.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTMD152511,ISO306/B5011 | 218 | °C |
| -- | ISO306/B120 | 220 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed,64.0mmSpan10 | ISO75-2/Bf | 224 | °C | |
| Linear thermal expansion coefficient | MD:-40to40°C | ASTME831,ISO11359-2 | 4.1E-05 | cm/cm/°C |
| TD:-40to40°C | ASTME831,ISO11359-2 | 7.4E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | ASTMD257 | 1E+16 | ohms·cm | |
| Dielectric Strength | 1.60mm,inAir | ASTMD149 | 23 | KV/mm |
| 1.60mm,inOil | ASTMD149 | 24 | KV/mm | |
| Comparative Tracking Index | CTI | UL746 | PLC1 | |
| Comparative Tracking Index | IEC60112 | 425 | V | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.0 | kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 12.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| UL flame retardant rating | 0.8mm,TestingbySABIC | UL94 | V-1 | |
| 2.0mm,TestingbySABIC | UL94 | 5VB5VA | ||
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.