Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ISO294-4 | 0.80 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 1.2 | % |
| Melt Volume flow Rate | 240°C/10.0kg | ISO1133 | 30.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 62.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 43.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 3.5 | % |
| Tensile Modulus | | ISO527-2 | 2000 | Mpa |
| Flexural Modulus | | ISO178 | 1800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | -- | ISO306/A50 | 160 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 102 | °C |
| Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 85.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 65.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 1MHz | IEC60250 | 2.90 | |
| Surface Resistivity | | IEC60093 | 1E+14 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 | |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation - MD | Break | ISO527-3 | >50 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ISO2039-2 | 103 | |
| Ball Indentation Hardness | | ISO2039-1 | 86.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.