Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.90 | % |
Melt Volume flow Rate | 240°C/10.0kg | ISO1133 | 15.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 115 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 60.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 3.2 | % |
Tensile Modulus | | ISO527-2 | 5400 | Mpa |
Flexural Modulus | | ISO178 | 4500 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | -- | ISO306/A50 | 180 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 114 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 164 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 100 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1MHz | IEC60250 | 0.013 | |
Relative Permittivity | 1MHz | IEC60250 | 2.90 | |
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Elongation - MD | Break | ISO527-3 | 3.2 | % |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 25 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 30 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 107 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.