ASA/PC GELOY™ XTPMFR10-WH5F007 SABIC INNOVATIVE SAUDI
141
- Unit Price:
- $3128 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Antistatic High mobility
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 30.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO 178 | 2720 | Mpa | |
| Flexural Stress | ISO 178 | 97.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 2680 | Mpa |
| -- | ISO 527-2/1 | 2680 | Mpa | |
| Tensile Elongation | Yield 4 | ASTM D638 | 4.0 | % |
| Yield 3 | ASTM D638 | 4.0 | % | |
| Yield | ISO 527-2/5, ISO 527-2/50 | 4.0 | % | |
| Break 4 | ASTM D638 | 58 | % | |
| Break 3 | ASTM D638 | 31 | % | |
| Break | ISO 527-2/5 | 50 | % | |
| Break | ISO 527-2/50 | 21 | % | |
| Tensile Strength | Yield 3 | ASTM D638 | 65.0 | Mpa |
| Yield 4 | ASTM D638 | 60.0 | Mpa | |
| Yield | ISO 527-2/5 | 61.0 | Mpa | |
| Yield | ISO 527-2/50 | 66.0 | Mpa | |
| Break 4 | ASTM D638 | 49.0 | Mpa | |
| Break 3 | ASTM D638 | 47.0 | Mpa | |
| Break | ISO 527-2/5 | 46.0 | Mpa | |
| Break | ISO 527-2/50 | 47.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 90.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 81.0 | °C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 96.0 | °C |
| -- | ISO 306/B120 | 98.0 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ISO 11359-2 | 6.3E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 6.3E-5 | cm/cm/°C |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 260°C, 1500 sec^-1 | ISO 11443 | 105 | Pa·s |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 到 90 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 230 到 270 | °C | ||
| Mold Temperature | 50 到 70 | °C | ||
| Drying Time | 2.0 到 4.0 | hr | ||
| Rear Temperature | 200 到 230 | °C | ||
| Middle Temperature | 220 到 260 | °C | ||
| Front Temperature | 230 到 270 | °C | ||
| Nozzle Temperature | 220 到 260 | °C | ||
| Hopper Temperature | 60 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | 85.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.0 mm, Testing by SABIC | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.