ASA/PC GELOY™ XP4034-BK1041 SABIC INNOVATIVE NANSHA
172
- Unit Price:
- $3543 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Weather resistance Antistatic High mobility
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Moisture Absorption | 24 hr | ASTM D570 | 0.25 | % |
| Melt Mass-Flow Rate | 280°C/3.8 kg | ASTM D1238 | 24 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTM D638 | 25 | % |
| Flexural Modulus | 50.0 mm Span | ASTM D790 | 2510 | Mpa |
| Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 88.0 | Mpa |
| Tensile Strength | Yield | ASTM D638 | 62.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 115 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 104 | °C | |
| Linear thermal expansion coefficient | Flow : -20 to 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| Across Flow : -20 to 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C | |
| Thermal Conductivity | ASTM C177 | 0.25 | W/m/K |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 95 到 105 | °C | ||
| Suggested Max Moisture | 0.040 | % | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 55 到 70 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 40 到 80 | % | ||
| Rear Temperature | 240 到 255 | °C | ||
| Middle Temperature | 245 到 260 | °C | ||
| Front Temperature | 250 到 265 | °C | ||
| Nozzle Temperature | 245 到 265 | °C | ||
| Back Pressure | 0.300 到 1.00 | Mpa | ||
| Screw Speed | 30 到 80 | rpm | ||
| Vent Depth | 0.038 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 30.0 | J |
| 23°C, Total Energy | ASTM D3763 | 47.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 110 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner | 60°, 无织构 | ASTM D523 | 94 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.