PC/PET XYLEX™ X8300 SABIC INNOVATIVE US
197
- Unit Price:
- $4314 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance
- Application Areas:Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40to0.60 | % |
| MD：3.20mm | 内部方法 | 0.50to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.050 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Melt mass flow rate | 265°C/2.16kg | ASTMD1238 | 15 | g/10min |
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 15.0 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.20 | g/cm³ | |
| ISO1183 | 1.17 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 4 | Break | ASTMD638 | 150 | % |
| Bending modulus 5 | ISO178 | 1700 | Mpa | |
| Bending strength 5,6 | ISO178 | 78.0 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 5.0 | % |
| Tensile modulus 2 | ASTMD638 | 1520 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 46.0 | Mpa |
| Yield | ASTMD638 | 47.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 1680 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 71.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 55.0 | Mpa |
| Break | ISO527-2/50 | 54.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | >5.0 | % |
| Break | ISO527-2/50 | >200 | % | |
| Tensile modulus | ISO527-2/1 | 1600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 79.0 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 75.0 | °C | |
| 1.8MPa,Unannealed,100mmSpan9 | ISO75-2/Ae | 80.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 78.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| MD：23to60°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD：23to60°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Vicat softening temperature | ASTMD152511 | 91.0 | °C | |
| ISO306/B120 | 96.0 | °C | ||
| thermal conductivity | ISO8302 | 0.23 | W/m/K | |
| BallPressureTest12 | 85°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 10 | kJ/m² |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| -10°C | ISO180/1A | 5.0 | kJ/m² | |
| 23°C | ISO180/1A | 8.0 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 95.0 | J |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 73 | J/m |
| 23°C | ASTMD256 | 1100 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D,10sec | ASTMD2240 | 74 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.539 | ||
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL94 | V-2 | |
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 750 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.