Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 7.8 | g/10min |
| monomer Content | | 内部方法 | 6.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus (2% Secant) | | ASTMD638,ISO527-2 | 130 | Mpa |
| Tensile Modulus (2% Secant) | | MPa | ASTM D-638 | 130 |
| Tensile Modulus (2% Secant) | | MPa | ISO 527-2 | 130 |
| Tensile Elongation | Break | ASTMD638,ISO527-2 | 590 | % |
| Tensile Strength(Break) | | MPa | ISO 527-2 | 18 |
| Tensile Strength(Break) | | MPa | ASTM D-638 | 18 |
| Tensile Strength | Yield | ASTMD638,ISO527-2 | 7.50 | Mpa |
| Tensile Strength | Break | ASTMD638,ISO527-2 | 18.0 | Mpa |
| Tensile Strength(Yield) | | MPa | ASTM D-638 | 7.5 |
| Tensile Strength(Yield) | | MPa | ISO 527-2 | 7.5 |
| Tensile Elongation?(Break) | | % | ASTM D-638 | 590 |
| Tensile Elongation?(Break) | | % | ISO 527-2 | 590 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature (DSC) | | 内部方法 | 100 | °C |
| Melting temperature | | ℃ | Internal Method | |
| Vicat Softening Temperature | | ISO306/A | 90.0 | °C |
| Vicat Softening Temperature | | ℃ | ISO 306/A | |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Peak Melting Temperature | | 内部方法 | 90.0 | °C |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | ℃ | | 260-290 |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Sealing Initial Temperature | | ℃ | Internal Method | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| monomer Content | | % | Internal Method | |
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | 7.8 |
| Melt index | 190℃/2.16kg | g/10min | ISO 1133 | 7.8 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.