PFA NEOFLON® AP-201 DAIKIN JAPAN
203
- Unit Price:
- $56210 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature strength copolymer High mobility Good liquidity High transparency
- Application Areas:Wire sheath
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 |
| Physical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792 | 2.14 到 2.16 | g/cm³ | |
| Apparent density | JIS K6891 | 1.00 到 1.40 | g/cm³ | |
| Melt mass flow rate | 372℃，5.0kg 372℃/5.0 kg | ASTM D1238 | 20 到 30 | g/10min |
| Water absorption rate | Saturation Saturation | ASTM D570 | < 0.010 | % |
| Apparent viscosity of melt | 380℃ 380℃ | 2.00E+6 到 2.50E+7 | mPa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D Shore D | ASTM D2240 | 60 到 70 | |
| Tensile strength | Yield Yield | JIS K6891 | 24.5 到 29.4 | Mpa |
| Tensile strain | Break Break | JIS K6891 | 350 到 450 | % |
| Bending modulus | ASTM D790 | 580 到 690 | Mpa | |
| Compressive modulus | ASTM D695 | 490 到 590 | Mpa | |
| compressive strength | 1% Strain 1% Strain | ASTM D695 | 4.90 到 5.90 | Mpa |
| 25% Strain 25% Strain | ASTM D695 | 31.4 到 33.3 | Mpa | |
| friction coefficient | 与钢 - 静态 与钢 - 静态 | 0.040 到 0.050 | ||
| Load deformation | 25℃，14 MPa 25°C, 14 MPa 2 2 | ASTM D621 | 2.50 到 3.00 | % |
| 25℃，14 MPa 25°C, 14 MPa 3 3 | ASTM D621 | 8.00 到 9.00 | % | |
| 100℃，6.9 MPa 100°C, 6.9 MPa 2 2 | ASTM D621 | 2.00 到 3.00 | % | |
| 100℃，6.9 MPa 100°C, 6.9 MPa 3 3 | ASTM D621 | 8.50 到 9.50 | % | |
| bending strength | ASTM D790 | No break |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.60 mm 1.6 mm | UL 94 | V-0 | ||
| Extreme Oxygen Index | 1.57 mm 1.57 mm | ASTM D2863 | > 95 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ASTM D4591 | 300 到 310 | °C | |
| Linear coefficient of thermal expansion | MD：20~100℃ MD：20 to 100℃ | ASTM D696 | 0.00012 | 1/℃ |
| Specific Heat | 1050 | J/kg/℃ | ||
| Thermal Conductivity | ASTM C177 | 0.26 | W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.