PC/PBT LNP™ COLORCOMP™ 6370-BK1G425L SABIC INNOVATIVE US
88
- Unit Price:
- $3621 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD：--2 | 内部方法 | 0.40to0.70 | % |
| TD：--3 | 内部方法 | 0.70to0.90 | % | |
| MD：--2 | 内部方法 | 0.30to0.40 | % | |
| MD：--3 | 内部方法 | 0.40to0.50 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.090 | % |
| Saturation,23°C | ISO62 | 0.50 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 24 | g/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 12.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 19.0 | cm3/10min | |
| Specific Volume | ASTMD792 | 0.700 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strain | Break | ASTMD638 | 4.0 | % |
| Yield | ASTMD638 | 3.0 | % | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 5380 | Mpa |
| ISO178 | 7750 | Mpa | ||
| Flexural Strength | ISO178 | 154 | Mpa | |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 150 | Mpa |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 138 | Mpa |
| Tensile Modulus | ASTMD638 | 9750 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 97.0 | Mpa |
| Tensile Strength | Break | ASTMD638 | 91.0 | Mpa |
| Tensile Modulus | ISO527-2/1 | 8500 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 105 | Mpa |
| Break | ISO527-2/5 | 3.00 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 3.0 | % |
| Break | ISO527-2/5 | 110 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 204 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 163 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 149 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 2.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 155 | °C |
| Vicat Softening Temperature | ASTMD152512 | 153 | °C | |
| -- | ISO306/B50 | 148 | °C | |
| -- | ISO306/B120 | 150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot-wire Ignition | HWI | UL746 | PLC1 | |
| High Amp Arc Ignition | HAI | UL746 | PLC3 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
| Arc Resistance | ASTMD495 | PLC5 | ||
| Dielectric Strength | 1.60mm,in Oil | ASTMD149 | 27 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 20 | KV/mm | |
| Dielectric Constant | 100Hz | ASTMD150 | 4.00 | |
| 1MHz | ASTMD150 | 4.00 | ||
| Volume Resistivity | ASTMD257 | 4.8E+15 | ohms·cm | |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Dissipation Factor? | 100Hz | ASTMD150 | 3E-03 | |
| 1MHz | ASTMD150 | 0.020 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 | J |
| 23°C,TotalEnergy | ASTMD3763 | 17.0 | J | |
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 9.0 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 109 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.