Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 266°C/5.0 kg | ASTM D1238 | 26 | g/10 min |
Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ASTM D638 | 2480 | Mpa |
Tensile Elongation | Yield | ASTM D638 | 4.0 | % |
Tensile Elongation | Break | ASTM D638 | 65 | % |
Tensile Strength | Yield | ASTM D638 | 63.0 | Mpa |
Tensile Strength | Break | ASTM D638 | 42.0 | Mpa |
Flexural Modulus | 50.0 mm Span | ASTM D790 | 2240 | Mpa |
Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 89.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTM D15255 | 102 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 78.0 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 3.0 到 4.0 | hr |
Suggested Shot Size | | | 30 到 80 | % |
Rear Temperature | | | 220 到 255 | °C |
Middle Temperature | | | 220 到 265 | °C |
Front Temperature | | | 245 到 275 | °C |
Nozzle Temperature | | | 245 到 275 | °C |
Back Pressure | | | 0.300 到 0.700 | Mpa |
Screw Speed | | | 40 到 70 | rpm |
Vent Depth | | | 0.038 到 0.076 | mm |
Drying Temperature | | | 80 到 90 | °C |
Suggested Max Moisture | | | 0.040 | % |
Processing (Melt) Temp | | | 245 到 275 | °C |
Mold Temperature | | | 60 到 80 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 65.0 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.1 mm | UL 94 | V-1 | |
Flame Rating | 1.5 mm | UL 94 | V-0 | |
Flame Rating | 2.5 mm | UL 94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.