PC/PBT XENOY™ 5720U-BK1066 SABIC INNOVATIVE US

Unit Price:
$4043 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.28	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%
Specific Volume		ASTM D792	0.850	cm³/g
Melt Mass-Flow Rate	250°C/2.16 kg	ASTM D1238	3.8	g/10 min
	Melt Mass-Flow Rate	250°C/5.0 kg	ASTM D1238, ISO 1133	11	g/10 min
		Melt Mass-Flow Rate	265°C/2.16 kg	ASTM D1238	6.0	g/10 min
			Melt Mass-Flow Rate	266°C/5.0 kg	ASTM D1238	20	g/10 min
			Melt Mass-Flow Rate	Melt Mass-Flow Rate	250°C/2.16 kg	ISO 1133	3.0	g/10 min
Melt Volume flow Rate	250°C/2.16 kg	ISO 1133	3.00	cm3/10min
	Melt Volume flow Rate	250°C/5.0 kg	ISO 1133	10.0	cm3/10min
		Melt Volume flow Rate	265°C/2.16 kg	ISO 1133	6.00	cm3/10min
		Melt Volume flow Rate	Melt Volume flow Rate	265°C/5.0 kg	ISO 1133	18.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	1.0 到 1.2	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 9, 10	ISO 178	71.0	Mpa
	Flexural Stress	Yield, 50.0 mm Span 8	ASTM D790	70.0	Mpa
	Flexural Stress	Flexural Stress	Break, 50.0 mm Span 8	ASTM D790	69.0	Mpa
Tensile Modulus	-- 2	ASTM D638	1830	Mpa
	Tensile Modulus	-- 3	内部方法	1830	Mpa
		Tensile Modulus	-- 4	ASTM D638	1810	Mpa
		Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	1790	Mpa
Tensile Elongation	Yield 7	ASTM D638	4.6	%
	Tensile Elongation	Yield 6	内部方法	4.6	%
		Tensile Elongation	Yield 5	ASTM D638	4.0	%
			Tensile Elongation	Yield	ISO 527-2/5	4.1	%
				Tensile Elongation	Yield	ISO 527-2/50	4.6	%
					Tensile Elongation	Break 7	ASTM D638	120	%
						Tensile Elongation	Break 6	内部方法	110	%
							Tensile Elongation	Break 5	ASTM D638	120	%
								Tensile Elongation	Break	ISO 527-2/5	110	%
								Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	120	%
Flexural Modulus	50.0 mm Span 8	ASTM D790	1660	Mpa
Flexural Modulus	Flexural Modulus	-- 9	ISO 178	1860	Mpa
Tensile Strength	Yield 5	ASTM D638	47.0	Mpa
	Tensile Strength	Yield 6	内部方法	45.0	Mpa
		Tensile Strength	Yield 7	ASTM D638	44.0	Mpa
			Tensile Strength	Yield	ISO 527-2/5	44.0	Mpa
				Tensile Strength	Yield	ISO 527-2/50	47.0	Mpa
					Tensile Strength	Break 7	ASTM D638	50.0	Mpa
						Tensile Strength	Break 6	内部方法	47.0	Mpa
							Tensile Strength	Break 5	ASTM D638	48.0	Mpa
							Tensile Strength	Tensile Strength	Break	ISO 527-2/5, ISO 527-2/50	43.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152513, ISO 306/B5013	119	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	122	°C
Linear thermal expansion coefficient	Flow : -40 to 95°C	ASTM E831	9.8E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -30 to 80°C	ISO 11359-2	9.8E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 95°C	ASTM E831	1.0E-4	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -30 to 80°C	ISO 11359-2	1.0E-4	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	108	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	117	°C
		Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12	ISO 75-2/Bf	109	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	83.0	°C
				Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	95.0	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12	ISO 75-2/Af	87.0	°C

Injection	Test Result	Unit
Drying Time	4.0 到 6.0	hr
Suggested Shot Size	50 到 80	%
Rear Temperature	245 到 265	°C
Middle Temperature	250 到 270	°C
Front Temperature	255 到 275	°C
Nozzle Temperature	255 到 270	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 80	rpm
Vent Depth	0.013 到 0.020	mm
Drying Temperature	110	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	260 到 275	°C
Mold Temperature	65 到 90	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	47	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	55	kJ/m²
Instrumented Dart Impact	-40°C, Energy at Peak	ASTM D3763	49.0	J
	Instrumented Dart Impact	-40°C, Total Energy	ASTM D3763	59.0	J
		Instrumented Dart Impact	-30°C, Energy at Peak	ASTM D3763	49.0	J
			Instrumented Dart Impact	-30°C, Total Energy	ASTM D3763	61.0	J
				Instrumented Dart Impact	-20°C, Energy at Peak	ASTM D3763	41.0	J
					Instrumented Dart Impact	-20°C, Total Energy	ASTM D3763	53.0	J
						Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	44.0	J
						Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	54.0	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Port of Loading	Unit Price
Huangpu port, China	6775 USD/MT