PC/PBT XENOY™ 6620U-1001 SABIC INNOVATIVE SHANGHAI
141
- Unit Price:
- $3418 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 55MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Low temperature impact re
- Application Areas:Electronic display Household daily necessiti Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 1.6to1.8 | % |
| TD：3.20mm | 内部方法 | 1.6to1.8 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.14 | % |
| Melt Mass-Flow Rate | 266°C/5.0kg | ASTMD1238 | 22 | g/10min |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 17.1 | cm3/10min |
| Specific Volume | ASTMD792 | 0.835 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 60.0 | Mpa | |
| Tensile Modulus | ISO527-2/1 | 1830 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 150 | % |
| Tensile Stress | Yield | ISO527-2/50 | 41.1 | Mpa |
| Break | ISO527-2/50 | 31.7 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | 19 | % |
| Yield | ISO527-2/50 | 3.9 | % | |
| Tensile Elongation | Yield | ASTMD638 | 4.2 | % |
| Tensile Modulus | ASTMD638 | 1780 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 43.7 | Mpa |
| Break | ASTMD638 | 32.9 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 1780 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 63.6 | Mpa |
| Flexural Modulus | ISO178 | 1700 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 75.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 75.0 | °C | |
| RTIStr | UL746 | 75.0 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 9.9E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 9.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 98.9 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 60.0 | °C | |
| Vicat Softening Temperature | ASTMD152510 | 123 | °C | |
| -- | ISO306/B50 | 119 | °C | |
| -- | ISO306/B120 | 122 | °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 50.5 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC0 | |
| Hot-wire Ignition | HWI | UL746 | PLC3 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
| Arc Resistance | ASTMD495 | PLC5 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 72 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 51 | kJ/m² |
| 23°C | ISO180/1A | 54 | kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 56.3 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.