PC/PBT XENOY™ X2420 BK1066 SABIC INNOVATIVE NANSHA
101
- Unit Price:
- $4371 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High impact resistance Dimensional stability Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Automotive Applications
- Color:--
- Grade:Chemical resistance
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 12.0 | cm3/10min |
| 300°C/1.2kg | ISO1133 | 26.0 | cm3/10min | |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.15到0.25 | % |
| TD:3.20mm | 内部方法 | 0.30到0.40 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.020 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 1 | ASTMD638 | 3800 | Mpa | |
| Surrender 2 | ASTMD638 | 50.0 | Mpa | |
| yield | ISO527-2/5 | 51.0 | Mpa | |
| Fracture 3 | ASTMD638 | 35.0 | Mpa | |
| crack | ISO527-2/5 | 37.0 | Mpa | |
| Surrender 4 | ASTMD638 | 3.0 | % | |
| yield | ISO527-2/5 | 3.0 | % | |
| crack | ISO527-2/5 | 7.0 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 3500 | Mpa |
| Bending strength 6 | Yield,50.0mmSpan | ASTMD790 | 90.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ISO306/B120 | 118 | °C | |
| Flow: -40 to 40 ° C | ASTME831 | 5E-05 | cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 8E-05 | cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| RTIElec | UL746 | 75.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 75.0 | °C | |
| RTI | UL746 | 75.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 111 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 101 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 15 | kJ/m² |
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | 95 | kJ/m² |
| 23°C | ISO179/1eU | 95 | kJ/m² | |
| 23°C | ASTMD256 | 210 | J/m | |
| -30°C9 | ISO180/1A | 8.0 | kJ/m² | |
| 23°C10 | ISO180/1A | 14 | kJ/m² | |
| 23°C | ASTMD4812 | 1600 | J/m | |
| -30°C11 | ISO180/1U | 74 | kJ/m² | |
| 23°C12 | ISO180/1U | 110 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 36.0 | J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.400mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.