PC/PBT XENOY™ VX5022-7001 SABIC INNOVATIVE US

Unit Price:
$3041 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow 2	内部方法	0.30 到 0.80	%
	Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.30 到 0.50	%
	Modeling Shrinkage	Modeling Shrinkage	Across Flow 2	内部方法	0.50 到 0.90	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.10	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.060	%
Melt Mass-Flow Rate	250°C/2.16 kg	ASTM D1238	16	g/10 min
	Melt Mass-Flow Rate	265°C/5.0 kg	ASTM D1238	50	g/10 min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	266°C/5.0 kg	ASTM D1238	50	g/10 min
Melt Volume flow Rate	250°C/2.16 kg	ISO 1133	13.0	cm3/10min
	Melt Volume flow Rate	250°C/5.0 kg	ISO 1133	28.0	cm3/10min
	Melt Volume flow Rate	Melt Volume flow Rate	265°C/5.0 kg	ISO 1133	40.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 6, 7	ISO 178	150	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 5	ASTM D790	145	Mpa
Tensile Modulus	-- 3	ASTM D638	7300	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	7100	Mpa
Tensile Elongation	Yield 4	ASTM D638	3.0	%
	Tensile Elongation	Yield	ISO 527-2/5	3.0	%
		Tensile Elongation	Break 4	ASTM D638	3.0	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/5	3.0	%
Flexural Modulus	50.0 mm Span 5	ASTM D790	5800	Mpa
Flexural Modulus	Flexural Modulus	-- 6	ISO 178	6300	Mpa
Tensile Strength	Yield 4	ASTM D638	125	Mpa
	Tensile Strength	Yield	ISO 527-2/5	110	Mpa
		Tensile Strength	Break 4	ASTM D638	125	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/5	110	Mpa
Tensile Strain		ISO 178	3.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152511, ISO 306/A5011	200	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ASTM D152512, ISO 306/B50, ISO 306/B120	145	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	4.0E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	2.5E-5	cm/cm/°C
		Linear thermal expansion coefficient	Flow : 23 to 60°C	ISO 11359-2	4.0E-5	cm/cm/°C
			Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	4.0E-5	cm/cm/°C
				Linear thermal expansion coefficient	Flow : 23 to 150°C	ISO 11359-2	2.4E-5	cm/cm/°C
					Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	1.0E-4	cm/cm/°C
						Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	6.9E-5	cm/cm/°C
							Linear thermal expansion coefficient	Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4	cm/cm/°C
								Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	1.0E-4	cm/cm/°C
								Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 150°C	ISO 11359-2	1.1E-4	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	180	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10	ISO 75-2/Bf	180	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10	ISO 75-2/Af	120	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	0.800 mm, in Oil	ASTM D149	31	KV/mm
	Dielectric Strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
		Dielectric Strength	3.20 mm, in Oil	ASTM D149	16	KV/mm
			Dielectric Strength	0.800 mm, in Oil	IEC 60243-1	31	KV/mm
				Dielectric Strength	1.60 mm, in Oil	IEC 60243-1	28	KV/mm
				Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Comparative Tracking Index	--	IEC 60112	250	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	100	V
Dissipation Factor?	1 MHz	ASTM D150, IEC 60250	0.014
	Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
		Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
		Dissipation Factor?	Dissipation Factor?	100 Hz	IEC 60250	1.0E-3
Surface Resistivity		IEC 60093	> 1.0E+16	ohms
Dielectric Constant	1 MHz	ASTM D150, IEC 60250	3.30
	Dielectric Constant	50 Hz	IEC 60250	3.10
		Dielectric Constant	60 Hz	IEC 60250	3.10
		Dielectric Constant	Dielectric Constant	100 Hz	IEC 60250	3.30
Volume Resistivity	--	ASTM D257	> 1.0E+15	ohms·cm
Volume Resistivity	Volume Resistivity	--	IEC 60093	> 1.0E+16	ohms·cm
Hot-wire Ignition		UL 746	PLC 0
High Amp Arc Ignition		UL 746	PLC 0

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTM D152512, ISO 306/B50, ISO 306/B120	20	%
Melt Viscosity	260°C, 1500 sec^-1	ISO 11443	215	Pa·s

Injection	Test Result	Unit
Drying Temperature	110 到 120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 270	°C
Mold Temperature	40 到 100	°C
Drying Time	2.0 到 4.0	hr
Rear Temperature	230 到 245	°C
Middle Temperature	240 到 255	°C
Front Temperature	245 到 265	°C
Nozzle Temperature	240 到 260	°C
Hopper Temperature	40 到 60	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C 9	ISO 179/1eU	40	kJ/m²
	Charpy Unnotched Impact Strength	-30°C	ISO 179/2U	50	kJ/m²
		Charpy Unnotched Impact Strength	23°C 9	ISO 179/1eU	40	kJ/m²
		Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/2U	55	kJ/m²
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	65.0	J
Unnotched Izod Impact Strength	-30°C	ASTM D4812	650	J/m
	Unnotched Izod Impact Strength	23°C	ASTM D4812	650	J/m
		Unnotched Izod Impact Strength	-30°C 10	ISO 180/1U	35	kJ/m²
		Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 10	ISO 180/1U	40	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R -Sale	ISO 2039-2	122
Ball Indentation Hardness	H 358/30	ISO 2039-1	205	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	750	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	2.0 mm	IEC 60695-2-12	850	°C
Oxygen Index		ISO 4589-2	23	%
Flame Rating	1.5 mm	UL 94	HB
Flame Rating	Flame Rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.