PC/PBT XENOY™ 1731J-1001 SABIC INNOVATIVE US
42
- Unit Price:
- $3410 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.60to0.80 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.28 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.080 | % | |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 250°C/5.0kg | ISO1133 | 8.0 | g/10min | |
| Specific Volume | ASTMD792 | 0.820 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 93.0 | Mpa | |
| Flexural Modulus | ISO178 | 2210 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Break | ISO527-2/50 | 58.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 5.0 | % |
| Break | ISO527-2/50 | 90 | % | |
| Tensile Elongation | Yield | ASTMD638 | 5.0 | % |
| Tensile Modulus | ASTMD638 | 2370 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 61.4 | Mpa |
| Break | ASTMD638 | 56.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 93.1 | Mpa |
| Tensile Modulus | ISO527-2/1 | 2330 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 100 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 116 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 93.0 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 107 | °C | |
| Vicat Softening Temperature | ASTMD152510 | 125 | °C | |
| -- | ISO306/B50 | 127 | °C | |
| -- | ISO306/B120 | 130 | °C | |
| RTIElec | UL746 | 75.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 75.0 | °C | |
| RTIStr | UL746 | 75.0 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 7.8E-05 | cm/cm/°C |
| MD：-40to95°C | ASTME831 | 8.3E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.6E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 99.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Arc Resistance | ASTMD495 | PLC5 | ||
| Hot-wire Ignition | HWI | UL746 | PLC2 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC2 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 61.5 | J |
| 23°C,TotalEnergy | ASTMD3763 | 61.1 | J | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 16 | kJ/m² |
| 23°C | ISO180/1A | 59 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.