Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD1 | 内部方法 | 0.50到0.90 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 14.0 | cm3/10min |
| Density / Specific Gravity | | ISO1183 | 1.30 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 140 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 90.0 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 3.0 | % |
| Tensile Modulus | | ISO527-2/1 | 4500 | Mpa |
| Flexural Modulus | | ISO178 | 4000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:23to80°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Thermal Conductivity | | ISO8302 | 0.19 | W/m/K |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
| -- | | ISO306/B50 | 135 | °C |
| -- | | ISO306/B120 | 130 | °C |
| 0.45MPa, Unannealed,100mm Span | | ISO75-2/Be | 115 | °C |
| 1.8MPa, Unannealed,100mm Span | | ISO75-2/Ae | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+14 | ohms·cm |
| Dielectric Strength | 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Relative Permittivity | 50Hz | IEC60250 | 3.30 | |
| Relative Permittivity | 60Hz | IEC60250 | 3.30 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.10 | |
| Dissipation Factor? | 50Hz | IEC60250 | 2E-03 | |
| Dissipation Factor? | 60Hz | IEC60250 | 2E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 35 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 35 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 3.0 | kJ/m² |
| Notched Izod Impact Strength | 0°C | ISO180/1A | 3.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 3.0 | kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 30 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 30 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 113 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 105 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.50mm,TestingbySABIC | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.