Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.11 | % |
Melt Volume flow Rate | 230°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | 450 | % |
Tensile Stress | Break | ISO527-2 | 32.0 | Mpa |
Tensile Stress | 5.0%Strain | ISO527-2 | 8.40 | Mpa |
Tensile Stress | 10%Strain | ISO527-2 | 12.0 | Mpa |
Tensile Stress | 50%Strain | ISO527-2 | 17.0 | Mpa |
Tensile Stress | 100%Strain | ISO527-2 | 16.0 | Mpa |
Tensile Modulus | | ISO527-2 | 160 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | TD | ISO11359-2 | 1.9E-04 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 205 | °C |
Vicat Softening Temperature | | ISO306/B50 | 61.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 100Hz | IEC60250 | 4.34 | |
Relative Permittivity | 1MHz | IEC60250 | 3.58 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Dielectric Strength | | IEC60243-1 | 15 | KV/mm |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dissipation Factor? | 100Hz | IEC60250 | 0.021 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.046 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A,15sec | ISO868 | 98 | |
Shore Hardness | Shore D,3sec | ISO868 | 51 | |
Shore Hardness | Shore D,15sec | ISO868 | 51 | |
Shore Hardness | Shore A,3sec | ISO868 | 98 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.