Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 1.1 | % |
Modeling Shrinkage | TD | ISO294-4 | 0.94 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.1 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.65 | % |
Moisture Absorption | Equilibrium,23°C,60%RH | ASTMD570 | 0.70 | % |
Melt Mass-Flow Rate | 200°C/2.16kg | ASTMD1238 | 17 | g/10min |
Melt Mass-Flow Rate | 200°C/2.16kg | ISO1133 | 16 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tab | 1000Cycles,CS-17Wheel | ASTMD1044 | 3.00 | mg |
Tensile Stress | Yield,23°C | ISO527-2 | 22.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 800 | % |
Tensile Strength | 23°C | ASTMD638 | 20.6 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 920 | % |
Flexural Modulus | 23°C | ASTMD790 | 95.1 | Mpa |
Flexural Modulus | 23°C | ISO178 | 75.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 65.0 | °C |
Brittleness Temperature | | ASTMD746 | <-70.0 | °C |
Vicat Softening Temperature | | ISO306/A50 | 120 | °C |
Melting temperature | | ISO11357-3 | 180 | °C |
Peak Melting Temperature | | ASTMD3418 | 170 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC60243-1 | 18 | KV/mm |
Dissipation Factor? | | ASTMD150 | 6E-04 | |
Dielectric Constant | | ASTMD150 | 4.90 | |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D | ASTMD2240 | 40 | |
Shore Hardness | Shore D | ISO868 | 40 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | HB | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
Resilience | | | 67 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.