Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr | ISO62 | 0.70 | % |
Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.70 | % |
Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.80 | % |
Melt Mass-Flow Rate | 220°C/2.16kg | ISO1133 | 8.5 | g/10min |
MediumDensity | | | 1.03 | g/cm³ |
SpecificHeatCapacityofMelt | | | 2140 | J/kg/°C |
ThermalConductivityofMelt | | | 0.16 | W/m/K |
Melt Volume flow Rate | 220°C/2.16kg | ISO1133 | 8.80 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Abrasion Resistance | | ISO4649 | 180 | mm³ |
Tensile Creep Modulus | 1hr | ISO899-1 | 28.0 | Mpa |
Nominal Tensile Strain at Break | | ISO527-2 | 800 | % |
Tensile Creep Modulus | 1000hr | ISO899-1 | 21.0 | Mpa |
Tensile Modulus | | ISO527-2 | 45.0 | Mpa |
Flexural Modulus | | ISO178 | 45.0 | Mpa |
Tensile Stress | 50%Strain | ISO527-2 | 6.70 | Mpa |
Tensile Stress | 100%Strain | ISO527-2 | 7.50 | Mpa |
Tensile Stress | Break | ISO527-2 | 29.0 | Mpa |
Tensile Stress | 5.0%Strain | ISO527-2 | 2.40 | Mpa |
Tensile Stress | 10%Strain | ISO527-2 | 3.20 | Mpa |
Tensile Strain | Break | ISO527-2 | >300 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO11357-3 | 193 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 2.3E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 2.3E-04 | cm/cm/°C |
Effective Thermal Diffusivity | | | 5.44E-08 | m²/s |
Glass Transition Temperature | | ISO11357-2 | -55.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 100Hz | IEC60250 | 4.80 | |
Relative Permittivity | 1MHz | IEC60250 | 4.70 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Dielectric Strength | | IEC60243-1 | 18 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
Tensile Impact Strength | 23°C | ISO8256/1 | 145 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D | ISO868 | 37 | |
Shore Hardness | Shore D,15sec | ISO868 | 33 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
FMVSS Flammability | | FMVSS302 | B | |
Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
EmissionofOrganicCompounds | | VDA277 | 10.0 | µgC/g |
Odor | | VDA270 | 4.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.