TPEE Hytrel® 3078 DUPONT USA
189
- Unit Price:
- $9946 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 18MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Thermal stability
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 5.0 | g/10min |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 5.00 | cm3/10min |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.60 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.80 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 0.940 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2 | 24.0 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 24.0 | Mpa |
| 10%Strain | ISO527-2 | 1.80 | Mpa | |
| 50%Strain | ISO527-2 | 5.00 | Mpa | |
| Tensile Strain | Break | ISO527-2 | >300 | % |
| Nominal Tensile Strain at Break | ISO527-2 | 900 | % | |
| Tensile Creep Modulus | 1hr | ISO899-1 | 22.0 | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 18.0 | Mpa |
| Flexural Modulus | ISO178 | 21.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittleness Temperature | ISO974 | -98.0 | °C | |
| Glass Transition Temperature | ISO11357-2 | -60.0 | °C | |
| Melting Temperature | ISO11357-3 | 177 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.8E-04 | cm/cm/°C |
| TD | ISO11359-2 | 2.1E-04 | cm/cm/°C | |
| Effective Thermal Diffusivity | 5.44E-08 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+14 | ohms | |
| Volume Resistivity | IEC60093 | 1E+13 | ohms·cm | |
| Dielectric Strength | IEC60243-1 | 18 | KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 5.40 | |
| 1MHz | IEC60250 | 5.30 | ||
| Dissipation Factor? | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.015 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore Hardness | Shore D,15sec | ISO868 | 26 | |
| Shore D | ISO868 | 30 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS Flammability | FMVSS302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.