Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D955 | 1.19 | % |
Modeling Shrinkage | | ASTM D955 | 1.1-1.3 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.5 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 18 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 1.2 | % |
Modeling Shrinkage | TD | ISO294-4 | 1.4 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.3 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.62 | % |
Moisture Absorption | Equilibrium,23°C,60%RH | ASTMD570 | 0.50 | % |
Melt Mass-Flow Rate | 220°C/2.16kg | ASTMD1238 | 25 | g/10min |
Melt Mass-Flow Rate | 220°C/2.16kg | ISO1133 | 28 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tab | 1000Cycles,CS-17Wheel | ASTMD1044 | 5.00 | mg |
Tensile Stress | Yield,23°C | ISO527-2 | 33.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 700 | % |
Tensile Strength | Yield,23°C | ASTMD638 | 30.9 | Mpa |
Tensile Strength | | ASTM D412/ISO 527 | 360 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | Yield,23°C | ASTMD638 | 770 | % |
Flexural Modulus | 23°C | ASTMD790 | 211 | Mpa |
Flexural Modulus | 23°C | ISO178 | 146 | Mpa |
Charpy impact strength | | ASTM D256/ISO 179 | NB | kg·cm/cm(J/M)ft·lb/in |
Tensile Elongation?(Break) | | ASTM D412/ISO 527 | 650 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ASTMD746 | <-70.0 | °C |
Burning Rate | | UL94 | HB(1.5mm) | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 102 | °C |
Melting Temperature | | | 200 | ℃(℉) |
Vicat Softening Temperature | | ISO306/A50 | 170 | °C |
Melting temperature | | ISO11357-3 | 200 | °C |
Peak Melting Temperature | | ASTMD3418 | 200 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC60243-1 | 19 | KV/mm |
Dissipation Factor? | | ASTMD150 | 6E-04 | |
Dielectric Constant | | ASTMD150 | 4.70 | |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D | ASTMD2240 | 55 | |
Shore Hardness | Shore D | ISO868 | 55 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | HB | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
Resilience | | | 50 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.