TPEE KEYFLEX® BT-1155D LG CHEM KOREA
140
- Unit Price:
- $7191 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Good stability
- Application Areas:Wire and cable applicatio pipeline Pipe fittings Application in the automo sporting goods Cable Electric wire Automotive sector Cable sheath
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | ASTMD995 | 1.1-1.5 | % |
| Moisture Absorption | (23°C,24hr) | ASTMD570 | 0.6 | % |
| Melt Mass-Flow Rate | 230℃/2.16Kg | ASTMD1238 | 25 | g/10min |
| Moisture Absorption | 23°C,24hr | ASTMD570 | 0.60 | % |
| Modeling Shrinkage | MD：3.20mm,InjectionMolded | ASTMD955 | 1.0to1.4 | % |
| Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238 | 14 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | 23°C | ASTMD638 | 13 | Mpa |
| Tensile Elongation?(Break) | 23°C | ASTMD638 | 800 | % |
| Flexural Modulus | 23°C | ASTMD790 | 196 | Mpa |
| Notched Izod Impact Strength | 23°C | ASTMD256 | NB | J/m |
| -40°C | ASTMD256 | 150 | J/m | |
| Tensile Strength | Yield,23°C,2.00mm,InjectionMolded | ASTMD638 | 13.2 | Mpa |
| Flexural Modulus | 23°C,6.40mm,InjectionMolded | ASTMD790 | 167 | Mpa |
| Tensile Elongation | Break,23°C,2.00mm,Injection | ASTMD638 | 850 | % |
| Tensile Strength | Break,23°C,2.00mm,Injection | ASTMD638 | 34.3 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak Melting Temperature | ASTMD3418 | 200 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm,Injection | ASTMD648 | 85.0 | °C |
| 0.45MPaUnannealed | ASTMD648 | 90 | °C | |
| Vicat Softening Temperature | Melting Temperature | ASTMD3418 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | ASTMD257 | >E13 | Ω.cm | |
| Comparative Tracking Index | SolutionA | IEC60112 | 600 | V |
| Dielectric Strength | 23°C,1.00mm | ASTMD149 | 26 | KV/mm |
| Volume Resistivity | 23°C | ASTMD257 | >1.0E+13 | ohms·cm |
| Insulation strength | ASTMD149 | 26 | KV/mm |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tearing Strength | 23°C | ASTMD624 | 147 | kN/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| DurometerHardness | ShoreD,23°C,InjectionMolded | ASTMD2240 | 52 | |
| Shore Hardness (Shore A) | ASTMD2240 | 55 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.