PPA AMODEL® AT-6115HS BK324 SOLVAY USA
93
- Unit Price:
- $7185 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Thermal stability Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Valves/valve components Industrial components Industrial applications Machine/mechanical compon Metal substitution Connector Parts under the hood of a Vehicle electronics Application in the automo Automotive Applications currency Shell
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | ASTMD955 | 1.0 | % |
| TD | ASTMD955 | 1.1 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break,23°C | ISO527-2 | 126 | Mpa |
| Break,24°C | ISO527-2 | 68.3 | Mpa | |
| Tensile Strain | Break,23°C | ISO527-2 | 4.1 | % |
| Break,24°C | ISO527-2 | 7.7 | % | |
| Tensile Modulus | ASTMD638 | 5380 | Mpa | |
| 23°C | ISO527-2 | 5200 | Mpa | |
| 100°C | ISO527-2 | 3100 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 3.4 | % |
| Flexural Modulus | ASTMD790 | 4410 | Mpa | |
| 23°C | ISO178 | 4270 | Mpa | |
| 100°C | ISO178 | 2340 | Mpa | |
| Flexural Strength | ASTMD790 | 165 | Mpa | |
| Flexural Stress | 23°C | ISO178 | 170 | Mpa |
| 100°C | ISO178 | 66.9 | Mpa | |
| Compressive Strength | ASTMD695 | 100 | Mpa | |
| Shearing Strength | ASTMD732 | 56.5 | Mpa | |
| Tensile Strength | ASTMD638 | 122 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak Melting Temperature | ASTMD3418 | 305 | °C | |
| Linear thermal expansion coefficient | MD：0to100°C | ASTME831 | 2.2E-05 | cm/cm/°C |
| MD：100to200°C | ASTME831 | 3E-05 | cm/cm/°C | |
| TD：0to100°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C | |
| Melting temperature | ISO11357-3 | 305 | °C | |
| Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 260 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 298 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 251 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 76 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | 55 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.