Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 2.0 | % |
Modeling Shrinkage | TD | ASTMD955 | 2.1 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.50 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2 | 75.2 | Mpa |
Tensile Stress | Yield,100°C | ISO527-2 | 38.6 | Mpa |
Tensile Stress | Break,23°C | ISO527-2 | 68.3 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 5.0 | % |
Tensile Strain | Yield,100°C | ISO527-2 | 3.7 | % |
Tensile Strain | Break,23°C | ISO527-2 | 15 | % |
Tensile Modulus | | ASTMD638 | 2760 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 2760 | Mpa |
Tensile Modulus | 100°C | ISO527-2 | 2100 | Mpa |
Flexural Modulus | | ASTMD790 | 2210 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2280 | Mpa |
Flexural Modulus | 100°C | ISO178 | 1720 | Mpa |
Flexural Strength | | ASTMD790 | 103 | Mpa |
Flexural Stress | 23°C | ISO178 | 79.3 | Mpa |
Flexural Stress | 100°C | ISO178 | 49.6 | Mpa |
Tensile Strength | | ASTMD638 | 83.4 | Mpa |
Shearing Strength | | ASTMD732 | 64.1 | Mpa |
Tensile Elongation | Break | ASTMD638 | 80 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Peak Melting Temperature | | ASTMD3418 | 315 | °C |
Linear thermal expansion coefficient | MD:0to100°C | ASTME831 | 7.8E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:100to200°C | ASTME831 | 1.3E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD:0to100°C | ASTME831 | 9.3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:100to200°C | ASTME831 | 1.4E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 315 | °C |
Deflection Temperature Under Load? | 0.45MPa,Annealed | ASTMD648 | 163 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 118 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 121 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 8E+13 | ohms |
Dielectric Constant | 60Hz | ASTMD150 | 3.30 | |
Dielectric Constant | 1MHz | ASTMD150 | 3.30 | |
Volume Resistivity | | ASTMD257 | 1.2E+16 | ohms·cm |
Dielectric Strength | | ASTMD149 | 17 | KV/mm |
Dissipation Factor? | 60Hz | ASTMD150 | 4E-03 | |
Dissipation Factor? | 1MHz | ASTMD150 | 0.016 | |
Comparative Tracking Index | | ASTMD3638 | >600 | V |
High Voltage Arc Tracking Rate | HVTR | UL746 | 12.0 | mm/min |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
PenetrationImpact3 | | ASTMD3763 | 4448 | N |
Instrumented Dart Impact | TotalEnergy | ASTMD3763 | 54.2 | J |
Notched Izod impact strength | 23°C | ISO180/1U | NoBreak | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.