PA9T Genestar™ G1350H-F02-BK KURARAY JAPAN

Unit Price:
$4750 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
110MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 1.00 mm		0.20	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 1.00 mm		0.80	%
Moisture Absorption	Equilibrium, 40°C, 95%RH		1.4	%
Melt Mass-Flow Rate	320°C/2.16 kg	ASTM D1238	42	g/10 min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	4.0	%
Flexural Modulus		ASTM D790	10000	Mpa
Flexural Strength		ASTM D790	230	Mpa
Tensile Strength		ASTM D638	180	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ASTM D648	290	°C
Melting temperature			306	°C
Glass Transition Temperature			125	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		ASTM D149	30	KV/mm
Comparative Tracking Index		UL 746	PLC 0
Dielectric Constant	10.0 GHz	ASTM D150	3.40
Volume Resistivity		ASTM D257	1.0E+16	ohms·cm
Dissipation Factor?	10.0 GHz	ASTM D150	9.0E-3

Flammability	Test Condition	Test Method	Test Result	Unit
Bar Flow Length	320°C, 500.0 µm		5.30	CM
Weld Elongation		ASTM D638	0.60	%
Weld Strength		ASTM D638	45.0	Mpa
Flame Rating		UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.