Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow : 1.00 mm | | 0.10 | % |
| Modeling Shrinkage | Across Flow : 1.00 mm | | 0.60 | % |
| Moisture Absorption | Equilibrium, 40°C, 95%RH | | 1.0 | % |
| Melt Mass-Flow Rate | 320°C/2.16 kg | ASTM D1238 | 21 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | Break | ASTM D638 | 4.0 | % |
| Flexural Modulus | | ASTM D790 | 11000 | Mpa |
| Flexural Strength | | ASTM D790 | 240 | Mpa |
| Tensile Strength | | ASTM D638 | 185 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648 | 285 | °C |
| Melting temperature | | | 306 | °C |
| Glass Transition Temperature | | | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | ASTM D149 | 30 | KV/mm |
| Comparative Tracking Index | | UL 746 | PLC 1 | |
| Dielectric Constant | 10.0 GHz | ASTM D150 | 3.40 | |
| Volume Resistivity | | ASTM D257 | 1.0E+16 | ohms·cm |
| Dissipation Factor? | 10.0 GHz | ASTM D150 | 0.010 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Bar Flow Length | 320°C, 500.0 µm | | 5.50 | CM |
| Weld Elongation | | ASTM D638 | 0.70 | % |
| Weld Strength | | ASTM D638 | 54.0 | Mpa |
| Flame Rating | | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.