TPV Santoprene™ 201-87 CELANESE USA
165
- Unit Price:
- $4367 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 27MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance High temperature resistan
- Application Areas:Electrical applications Electrical components diaphragm Pipe fittings Movable hinge household electrical appl Home appliance components Parts under the hood of a Application in the automo Automotive Applications Consumer product applicat
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Detergent | ISO188 | f4 | ||
| UL749 | f3 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittleness Temperature | ASTMD746 | -54.0 | °C | |
| ISO812 | -54.0 | °C | ||
| RTIElec | UL746 | 100 | °C | |
| RTIStr | 1.0mm | UL746 | 90.0 | °C |
| 1.5mm | UL746 | 90.0 | °C | |
| 3.0mm | UL746 | 95.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 23°C,2.00mm | ASTMD149 | 32 | KV/mm |
| Dielectric Constant | 23°C,1.98mm | ASTMD150 | 2.40 | |
| 23°C,1.98mm | IEC60250 | 2.40 | ||
| Comparative Tracking Index | CTI | UL746 | PLC0 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Amp Arc Ignition | PLC | UL746 | PLC5 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
| Hot-wire Ignition | 1.0mm | UL746 | PLC4 | |
| 1.5mm | UL746 | PLC3 | ||
| 3.0mm | UL746 | PLC2 |
| Aging Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Change in Volume | 125°C,70hr,在IRM903油中 | ISO1817 | 48 | % |
| Change in Tensile Strength in Air | 150°C,168hr | ISO188 | -15 | % |
| Change in Ultimate Elongation in Air | 150°C,168hr | ASTMD573 | -16 | % |
| Change in Durometer Hardness in Air | ShoreA,150°C,168hr | ASTMD573 | 2.0 | |
| Change in Shore Hardness in Air | ShoreA,150°C,168hr | ISO188 | 2.0 | |
| Change in Tensile Strength | 125°C,70hr,inIRM903Oil | ASTMD471 | -29 | % |
| ChangeinTensileStress | 125°C,70hr,inIRM903Oil | ISO1817 | -29 | % |
| ChangeinUltimateElongation | 125°C,70hr,inIRM903Oil | ASTMD471 | -32 | % |
| ChangeinTensileStrainatBreak | 125°C,70hr,inIRM903Oil | ISO1817 | -32 | % |
| Change in Volume | 125°C,70hr,在IRM903油中 | ASTMD471 | 48 | % |
| Change in Tensile Strength in Air | 150°C,168hr | ASTMD573 | -15 | % |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compression Set | 70°C,22hr | ISO815 | 36 | % |
| 125°C,70hr | ISO815 | 44 | % | |
| Tensile Stress(Across Flow) | 100%Strain,23°C | ASTMD412 | 7.10 | Mpa |
| 100%Strain,23°C | ISO37 | 7.10 | Mpa | |
| Tensile Strength (flow) | Break,23°C | ASTMD412 | 15.0 | Mpa |
| Tensile Strength (TD) | Break,23°C | ISO37 | 15.0 | Mpa |
| Tensile Elongation(Across Flow) | Break,23°C | ASTMD412 | 580 | % |
| Break,23°C | ISO37 | 580 | % | |
| Tearing Strength (MD) | 23°C | ASTMD624 | 54.0 | kN/m |
| TearStrength-AcrossFlow3 | 23°C | ISO34-1 | 54 | kN/m |
| Compression Set | 70°C,22hr | ASTMD395B | 36 | % |
| 125°C,70hr | ASTMD395B | 44 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore Hardness | Shore A,15sec,23°C | ISO868 | 93 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.