Technical Data Sheet
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ASTMD746 | -62.0 | °C |
Brittleness Temperature | | ISO812 | -62.0 | °C |
RTIElec | | UL746 | 100 | °C |
RTIStr | 1.1mm | UL746 | 90.0 | °C |
RTIStr | 3.0mm | UL746 | 95.0 | °C |
Aging Properties | Test Condition | Test Method | Test Result | Unit |
---|
Change in Tensile Strength in Air | 150°C,168hr | ASTMD573 | -10 | % |
Change in Tensile Strength in Air | 150°C,168hr | ISO188 | -10 | % |
Change in Durometer Hardness in Air | ShoreA,150°C,168hr | ASTMD573 | 2.0 | |
Change in Shore Hardness in Air | ShoreA,150°C,168hr | ISO188 | 2.0 | |
Change in Ultimate Elongation in Air | 150°C,168hr | ASTMD573 | -26 | % |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compression Set | 70°C,22hr | ASTMD395B | 25 | % |
Tensile Stress(Across Flow) | 100%Strain,23°C | ASTMD412 | 1.50 | Mpa |
Tensile Stress(Across Flow) | 100%Strain,23°C | ISO37 | 1.50 | Mpa |
Tensile Strength (flow) | Break,23°C | ASTMD412 | 3.60 | Mpa |
Tensile Strength (TD) | Break,23°C | ISO37 | 3.60 | Mpa |
Tensile Elongation(Across Flow) | Break,23°C | ASTMD412 | 410 | % |
Tensile Elongation(Across Flow) | Break,23°C | ISO37 | 410 | % |
Compression Set | 70°C,22hr | ISO815 | 25 | % |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A,15sec,23°C | ISO868 | 49 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.1mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.