TPV Santoprene™ 201-64 CELANESE USA
57
- Unit Price:
- $4967 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 17MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Detergent | ISO188 | f4 | ||
| UL749 | f3 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | 1.0mm | UL746 | 90.0 | °C |
| 1.5mm | UL746 | 90.0 | °C | |
| 3.0mm | UL746 | 95.0 | °C | |
| Brittleness Temperature | ASTMD746,ISO812 | -60.0 | °C | |
| RTIElec | UL746 | 100 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 23°C,2.00mm | ASTMD149 | 30 | KV/mm |
| Hot-wire Ignition | HWI | UL746 | PLC2 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
| High Amp Arc Ignition | PLC | UL746 | PLC6 | |
| Dielectric Constant | 23°C,1.98mm | ASTMD150,IEC60250 | 2.30 | |
| Comparative Tracking Index | CTI | UL746 | PLC0 |
| Aging Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Change in Durometer Hardness | 支撐A,125°C,70hr,在IRM903油中 | ASTMD471 | -20 | |
| 支撐A,125°C,168hr,在ASTM#1油中 | ASTMD471 | -14 | ||
| 支撐A,125°C,1000hr,在防冻剂中，50/50V/V/水 | ASTMD471 | -4.0 | ||
| Shore A,125°C,70hr,在IRM903油中 | ISO1817 | -20 | ||
| Shore A,125°C,168hr,在ASTM#1油中 | ISO1817 | -14 | ||
| Shore A,125°C,1000hr,在防冻剂中，50/50V/V/水 | ISO1817 | -4.0 | ||
| Continuous Use Temperature | 1008hr | 自定标准 | 135 | °C |
| Change in Durometer Hardness in Air | Shore A,150°C,168hr | ASTMD573,ISO188 | 2.0 | |
| Change in Ultimate Elongation in Air | 150°C,168hr | ASTMD573,ISO188 | 6.0 | % |
| Change in Volume | 125°C,70hr,在IRM903油中 | ASTMD471,ISO1817 | 87 | % |
| Change in Ultimate Elongation | 125°C,70hr,在IRM903油中 | ASTMD471,ISO1817 | -49 | % |
| 125°C,168hr,在ASTM#1油中 | ASTMD471,ISO1817 | -35 | % | |
| 125°C,1000hr,在防冻剂中，50/50V/V/水 | ASTMD471,ISO1817 | -21 | % | |
| Change in Tensile Strength | 125°C,70hr,在IRM903油中 | ASTMD471,ISO1817 | -30 | % |
| 125°C,168hr,在ASTM#1油中 | ASTMD471,ISO1817 | -21 | % | |
| 125°C,1000hr,在防冻剂中，50/50V/V/水 | ASTMD471,ISO1817 | -7.0 | % | |
| Change in Tensile Strength in Air | 150°C,168hr | ASTMD573,ISO188 | -12 | % |
| Change in Mass | 121°C,168hr,在自动传动液中 | ASTMD471 | 72 | % |
| 125°C,168hr,在ASTM#1油中 | ASTMD471 | 39 | % | |
| 125°C,1000hr,在防冻剂中，50/50V/V/水 | ASTMD471 | 13 | % | |
| 125°C,1000hr,在防冻剂中，50/50V/V/水 | ISO1817 | 13 | % | |
| 125°C,168hr,在ASTM#1油中 | ISO1817 | 39 | % | |
| 121°C,168hr,在自动传动液中 | ISO1817 | 72 | % |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tearing Strength (MD) | 23°C3 | ASTMD624 | 23.0 | kN/m |
| 23°C4 | ISO34-1 | 23 | kN/m | |
| Tensile Stress(Across Flow) | 100%Strain,23°C | ASTMD412,ISO37 | 2.60 | Mpa |
| Tensile Strength (flow) | Break,23°C | ASTMD412,ISO37 | 7.00 | Mpa |
| Tensile Elongation(Across Flow) | Break,23°C | ASTMD412,ISO37 | 450 | % |
| Compression Set | 70°C,22hr5 | ASTMD395B | 18 | % |
| 125°C,70hr5 | ASTMD395B | 44 | % | |
| 70°C,22hr6 | ISO815 | 18 | % | |
| 125°C,70hr6 | ISO815 | 44 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore Hardness | Shore A,15sec,23°C | ISO868 | 69 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.