Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:2.54mm | ASTMD955 | 0.80 | % |
Modeling Shrinkage | TD:2.54mm | ASTMD955 | 0.80 | % |
Modeling Shrinkage | TD:2.54mm | ISO2577 | 0.80 | % |
Modeling Shrinkage | MD:2.54mm | ISO2577 | 0.80 | % |
Melt Mass-Flow Rate | 190°C/8.7kg | ASTMD1238 | 4.0 | g/10min |
Melt Mass-Flow Rate | 190°C/8.7kg | ISO1133 | 4.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | 1000Cycles,1000g,H-18Wheel | ISO4649 | 30.0 | mg |
Taber Abrasion Resistance | 1000Cycles,1000g,H-18Wheel | ASTMD1044 | 30.0 | mg |
Flexural Modulus | 23°C | ASTMD790 | 29.9 | Mpa |
Flexural Modulus | 23°C | ISO178 | 26.9 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD15254 | 80.0 | °C |
Vicat Softening Temperature | | ISO306/50 | 80.0 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compression Set | 23°C,22hr | ASTMD395B | 16 | % |
Compression Set | 70°C,22hr | ASTMD395B | 40 | % |
Compression Set | 23°C,22hr | ISO815 | 16 | % |
Compression Set | 70°C,22hr | ISO815 | 40 | % |
Tensile Stress | Yield | ISO37 | 36.6 | Mpa |
Tensile Stress | 100%Strain | ASTMD412 | 5.50 | Mpa |
Tensile Stress | 100%Strain | ISO37 | 5.50 | Mpa |
Tensile Stress | 300%Strain | ASTMD412 | 9.70 | Mpa |
Tensile Stress | 300%Strain | ISO37 | 9.70 | Mpa |
Tensile Strength | Yield | ASTMD412 | 36.6 | Mpa |
Tensile Elongation | Break | ASTMD412 | 610 | % |
Tensile Elongation | Break | ISO37 | 610 | % |
Tearing Strength | | ASTMD624 | 87.6 | kN/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 85 | |
Shore Hardness | Shore A | ISO868 | 85 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
The Yellow Index | -- | DIN6167 | <10 | YI |
The Yellow Index | -- | ASTME313 | <10 | YI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.