Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 160°C/8.7kg | | 35.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Abrasion2 | -- | ASTMD395 | 43 | mm³ |
Abrasion2 | -- | DIN53516 | 43 | mm³ |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
TMA4 | High:635.0µm | 内部方法 | 145 | °C |
TMA4 | Low:635.0µm | 内部方法 | 110 | °C |
Melting temperature | | 内部方法 | 98.9to130 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compression Set | 23°C,70hr | ASTMD395 | 40 | % |
Compression Set | 70°C,24hr | ASTMD395 | 80 | % |
Compression Set | 23°C,70hr | DIN53517 | 35 | % |
Compression Set | 70°C,24hr | DIN53517 | 60 | % |
Shore Hardness | | ASTMD2632 | 60 | % |
TensileSet3 | 200%Strain | ASTMD412 | 8 | % |
TensileSet3 | 200%Strain | DIN53504 | 8 | % |
Tensile Strength | 100%Strain,0.635mm | ASTMD412 | 2.34 | Mpa |
Tensile Strength | 100%Strain,0.635mm | DIN53504 | 1.40 | Mpa |
Tensile Strength | 300%Strain,0.635mm | ASTMD412 | 4.07 | Mpa |
Tensile Strength | 300%Strain,0.635mm | DIN53504 | 2.40 | Mpa |
Tensile Strength | Break,0.635mm | ASTMD412 | 7.52 | Mpa |
Tensile Strength | Break,0.635mm | DIN53504 | 10.0 | Mpa |
Tensile Strain | Break,0.635mm | ASTMD412 | 720 | % |
Tensile Strain | Break,0.635mm | DIN53504 | 900 | % |
TearStrength4 | 0.635mm | ASTMD624 | 35.9 | kN/m |
TearStrength4 | 0.635mm | DIN53515 | 25 | kN/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A,Injection | ASTMD2240 | 56 | |
Shore Hardness | Shore D,Injection | ASTMD2240 | 15 | |
Shore Hardness | Shore A,Injection | DIN53505 | 55 | |
Shore Hardness | Shore D,Injection | DIN53505 | 15 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.