Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Volume flow Rate | 190°C/21.6kg | ISO1133 | 30.0 | cm3/10min |
| Modeling Shrinkage | | | 2.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Abrasion2 | | ISO4649 | 80 | mm³ |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | | 125to190 | °C |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tearing Strength | | ASTMD624 | 52.5 | kN/m |
| Tearing Strength | | ISO34-1 | 45 | kN/m |
| Compression Set | 23°C,24hr | ASTMD395 | 35 | % |
| Compression Set | 70°C,24hr | ASTMD395 | 45 | % |
| Compression Set | 23°C,24hr | ISO815 | 35 | % |
| Compression Set | 70°C,24hr | ISO815 | 58 | % |
| Compression Set | 巴肖氏弹性 | ISO815 | 25 | % |
| Tensile Elongation | Break | ASTMD412 | 650 | % |
| Tensile Elongation | Break | DIN53504 | 650 | % |
| Tensile Stress | Break | DIN53504 | 30.0 | Mpa |
| Tensile Stress | 100%Strain | ASTMD412 | 3.93 | Mpa |
| Tensile Stress | 100%Strain | DIN53504 | 3.30 | Mpa |
| Tensile Stress | 300%Strain | ASTMD412 | 6.55 | Mpa |
| Tensile Stress | 300%Strain | DIN53504 | 5.80 | Mpa |
| Tensile Strength | Break | ASTMD412 | 15.2 | Mpa |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore A,Injection | ASTMD2240 | 75 | |
| Shore Hardness | Shore D,Injection | ASTMD2240 | 25 | |
| Shore Hardness | Shore A,Injection | ISO868 | 75 | |
| Shore Hardness | Shore D,Injection | ISO868 | 25 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.