Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190°C/10.0kg | ASTMD1238 | 10to20 | g/10min |
Melt Mass-Flow Rate | 190°C/21.6kg | ASTMD1238 | 10to40 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | | ASTMD1044 | 45.0 | mg |
Abrasion-DIN | | DIN53516 | 25 | mm³ |
Tensile Modulus | | ASTM D-638 | 31 | Mpa |
Tensile Modulus | Injection | ASTMD412 | 31.0 | Mpa |
Tensile Elongation | Break | ASTM D-412 | 580 | % |
Flexural Modulus | Injection | ASTMD790 | 29.0 | Mpa |
Flexural Modulus | | ASTM D-790 | 44.8 | Mpa |
Tearing Strength | | ASTM D-624 | 130 | kN/m |
Tensile Strength(Break) | | ASTM D-412 | 36.5 | Mpa |
Tensile Stress (100%) | | ASTM D-412 | 10.3 | Mpa |
Tensile Stress (300%) | | ASTM D-412 | 17.2 | Mpa |
hardness | shoreA | ASTM D-2240 | 91 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Glass Transition Temperature | | 内部方法 | -35.0 | °C |
SofteningPoint DMA | | 内部方法 | 100 | °C |
Vicat Softening Temperature | | ASTMD1525 | 120 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 100%Strain | ASTMD412 | 12.4 | Mpa |
Tensile Stress | 300%Strain | ASTMD412 | 27.6 | Mpa |
Tensile Strength | | ASTMD412 | 37.2 | Mpa |
Tensile Elongation | Break | ASTMD412 | 460 | % |
Tearing Strength | | ASTMD624 | 128 | kN/m |
Compression Set | 23°C,22hr | ASTMD395B | 25 | % |
Compression Set | 70°C,22hr | ASTMD395B | 45 | % |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 90 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D-792 | 1.13 | g/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.