Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 200°C/21.6kg | ASTMD1238 | 20to60 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | | ASTMD1044 | 25.0 | mg |
Abrasion-DIN | | DIN53516 | 25 | mm³ |
Tensile Modulus | Injection | ASTMD412 | 20.7 | Mpa |
Flexural Modulus | Injection | ASTMD790 | 24.8 | Mpa |
Tearing Strength | | ISO 34-1 | 70 | kN/m |
hardness | Shore A | ISO 868 | 87 | |
Tensile Stress | Break | ISO 527-2 | 50 | Mpa |
Tensile Stress | 100%strain | ISO 37 | 5.5 | Mpa |
Tensile Stress | 300%strain | ISO 37 | 9.5 | Mpa |
Tensile Strain | Break | ISO 527-2 | 650 | % |
Compression Set | 23℃ | ISO 815 | 25 | % |
Compression Set | 70℃ | ISO 815 | 35 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD1525 | 110 | °C |
Glass Transition Temperature | | 内部方法 | -40.0 | °C |
SofteningPoint DMA | | 内部方法 | 100 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 100%Strain | ASTMD412 | 6.89 | Mpa |
Tensile Stress | 300%Strain | ASTMD412 | 15.2 | Mpa |
Tensile Strength | | ASTMD412 | 41.4 | Mpa |
Tensile Elongation | Break | ASTMD412 | 590 | % |
Tearing Strength | | ASTMD624 | 109 | kN/m |
Compression Set | 23°C,22hr | ASTMD395B | 25 | % |
Compression Set | 70°C,22hr | ASTMD395B | 35 | % |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 85 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.9mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1.19 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.