TPU IROGRAN® A78P4766 HUNTSMAN GERMANY
154
- Unit Price:
- $11106 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 46MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Foggy surface
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：Injection | ASTMD955 | 1.0 | % |
| Melt Volume flow Rate | 190°C/21.6kg | 110 | cm3/10min | |
| Shore Hardness (Shore A) | ISO 7619 | 80 | Shore A | |
| Shore Hardness (Shore D) | ISO 7619 | 31 | Shore D |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Abrasion2 | ISO4649 | 40 | mm³ | |
| Tensile Modulus (100%) | DIN 53504 | 4.0 | Mpa | |
| Tensile Modulus (300%) | DIN 53504 | 7.0 | Mpa | |
| Compression Set (24h 23℃) | ISO 815 | 24 | % | |
| Compression Set (24h 70℃) | ISO 815 | 42 | % | |
| Taber Abrasion Resistance | ISO 4649 | 40 | mm³ | |
| Tensile Strength | DIN 53504 | 34 | Mpa | |
| Tensile Elongation | Break | DIN 53504 | 670 | % |
| Tearing Strength | ISO 34-1 | 76 | N/mm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔融温度范围下限 | Huntsman | 127 | °C | |
| Peak Crystallization Temperature | Huntsman | 156 | °C | |
| TMA3 | High:635.0µm | 内部方法 | 190 | °C |
| Low:635.0µm | 内部方法 | 165 | °C |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Break | ASTMD412 | 27.6 | Mpa |
| Tearing Strength | ASTMD624 | 71.8 | kN/m | |
| ISO34-1 | 40 | kN/m | ||
| Tensile Stress | Break | DIN53504 | 30.0 | Mpa |
| 100%Strain | ASTMD412 | 5.79 | Mpa | |
| 100%Strain | DIN53504 | 5.20 | Mpa | |
| 300%Strain | ASTMD412 | 9.65 | Mpa | |
| 300%Strain | DIN53504 | 8.00 | Mpa | |
| Compression Set | 23°C,24hr | ASTMD395 | 20 | % |
| 70°C,24hr | ASTMD395 | 40 | % | |
| 23°C,24hr | ISO815 | 20 | % | |
| 70°C,24hr | ISO815 | 40 | % | |
| Tensile Elongation | Break | ASTMD412 | 800 | % |
| Break | DIN53504 | 800 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore Hardness | Shore A,Injection | ASTMD2240 | 82 | |
| Shore D,Injection | ASTMD2240 | 30 | ||
| Shore A,Injection | ISO868 | 82 | ||
| Shore D,Injection | ISO868 | 30 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.