Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40to0.70 | % |
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 23 | g/10min |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 23.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTMD638 | 55 | % |
Flexural Modulus | | ISO178 | 2200 | Mpa |
Flexural Stress | | ISO178 | 67.0 | Mpa |
Tensile Strength | Yield | ASTMD638 | 43.0 | Mpa |
Flexural Modulus | | ASTMD790 | 2160 | Mpa |
Flexural Strength | | ASTMD790 | 63.3 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 46.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 33.0 | Mpa |
Tensile Strain | Break | ISO527-2/50 | 20 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 80.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ISO75-2/A | 97.0 | °C |
Deflection Temperature Under Load? | Annealed | ASTMD648 | 95 | °C |
Deflection Temperature Under Load? | Unannealed | ASTMD648 | 85 | °C |
Vicat Softening Temperature | | ASTMD15256 | 105 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 105 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 94.0 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 105 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.