Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.07 | |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 4 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃，10kg | ASTM D-1238 | 4 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| IZOD Notch Impact Strength | 1/4"，23℃ | ASTM D-256 | 25(4.6) | kg-cm/cm(ft-lb/im) |
| Tensile strength | 1/8“，6mm/min | ASTM D-638 | 450(6380) | kg/cm2(lb/in2) |
| Tensile Strength | | ASTM D638/ISO 527 | 420 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 550 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | 1/4“，2.8mm/min | ASTM D-790 | 660(9330) | kg/cm2(lb/in2) |
| Izod notch impact strength | | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1/4“,120℃/hr，Annealed | ASTM D-648 | 95(203) | ℃（℉） |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 95 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 105 | ℃（℉） |
| Vicat Softening Temperature | 1/8“,50℃/hr | ASTM D-1525 | 105(221) | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | | ASTM D-523 | 93 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.