Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16 kg | ASTM D1238 | 5.0 | g/10 min |
| Mooney Viscosity | ML 1+4, 121°C | ASTM D1646 | 8 | MU |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus (100% Secant) | Compression Molded | ASTM D638 | 2.35 | Mpa |
| Flexural Modulus - 1% Secant | Compression Molded | ASTM D790 | 10.8 | Mpa |
| Tensile Elongation | Break, Compression Molded | ASTM D638 | > 1000 | % |
| Tensile Strength | Break, Compression Molded | ASTM D638 | 6.18 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | 内部方法 | 61.0 | °C |
| Glass Transition Temperature | | 内部方法 | -53.0 | °C |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tearing Strength | | ASTM D624 | 37.3 | kN/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore A, 1 sec, Compression Molded | ASTM D2240 | 66 | |
| Shore Hardness | Shore D, 1 sec, Compression Molded | ASTM D2240 | 17 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.