POE AFFINITY™ PL-1880G DOW USA
59
- Unit Price:
- $2920 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.0 | g/10min |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTMD1525 | 86.0 | °C | |
| Melting temperature (DSC) | 内部方法 | 99.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Thickness - Tested) | 51 | µm | ||
| Secant Modulus | 2%Secant,MD:51μm | ASTMD882 | 91.7 | Mpa |
| 2%Secant,TD:51μm | ASTMD882 | 92.4 | Mpa | |
| Tensile Elongation | MD:Break,51μm | ASTMD882 | 620 | % |
| TD:Break,51μm | ASTMD882 | 630 | % | |
| Tensile Strength | MD:Yield,51μm | ASTMD882 | 7.24 | Mpa |
| TD:Yield,51μm | ASTMD882 | 6.89 | Mpa | |
| MD:Break,51μm | ASTMD882 | 58.6 | Mpa | |
| TD:Break,51μm | ASTMD882 | 44.7 | Mpa | |
| Gardner Impact | 51µm | ASTMD1709B | >830 | g |
| Film Puncture Force | 51µm | 内部方法 | 22.3 | J/cm³ |
| Film Puncture Energy | 51µm | 内部方法 | 8.81 | J |
| Film Puncture Force | 51µm | 内部方法 | 92.5 | N |
| Elmendorf Tear Strength | MD:51µm | ASTMD1922 | 550 | g |
| TD:51µm | ASTMD1922 | 720 | g | |
| Peak Melting Temperature | 51µm | 内部方法 | 85.0 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 50.8µm | ASTMD1003 | 1.1 | % |
| Transmittance | 50.8µm | ASTMD1746 | 83.0 | |
| Gloss | 20°,50.8µm | ASTMD2457 | 141 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.