Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 36g/10min | g/10min | |
| Density | ASTM D792/ISO 1183 | 1.04 | ||
| Modeling Shrinkage | ASTM D955 | 0.60% | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | ASTM D638/ISO 527 | 60 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTM D790/ISO 178 | 3200 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 100 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 3.0% | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | |
| Izod notch impact strength | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 135 | ℃（℉） | |
| ASTM D648/ISO 75 | 125 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | ISO 14782 | 0.50% | % | |
| Transmittance | ASTM D1003/ISO 13468 | 90% | % | |
| Refractive index of light | ASTM D542/ISO 489 | 1.540 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.