PEI ULTEM™ Resin AUT200AR BK1E157S SABIC INNOVATIVE SPAIN
95
- Unit Price:
- $16548 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 1.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % | |
| Melt Mass-Flow Rate | 337°C/6.7 kg | ASTM D1238 | 18 | g/10 min |
| Melt Volume flow Rate | 360°C/5.0 kg | ISO 1133 | 25.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO 527-2/5 | 105 | Mpa |
| Break | ISO 527-2/5 | 85.0 | Mpa | |
| Tensile Strain | Yield | ISO 527-2/5 | 6.0 | % |
| Break | ISO 527-2/5 | 60 | % | |
| Tensile Modulus | ISO 527-2/1 | 3200 | Mpa | |
| Flexural Modulus | ISO 178 | 3300 | Mpa | |
| Flexural Stress | ISO 178 | 160 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 5 | ISO 75-2/Be | 200 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 5 | ISO 75-2/Ae | 190 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4 | ISO 75-2/Af | 193 | °C | |
| Vicat Softening Temperature | -- | ISO 306/A50 | 215 | °C |
| -- | ISO 306/B50 | 211 | °C | |
| -- | ISO 306/B120 | 212 | °C | |
| Linear thermal expansion coefficient | Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Across Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 150 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 350 到 400 | °C | ||
| Mold Temperature | 135 到 165 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 330 到 400 | °C | ||
| Middle Temperature | 340 到 400 | °C | ||
| Front Temperature | 345 到 400 | °C | ||
| Nozzle Temperature | 345 到 400 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 33.0 | J |
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 5.0 | kJ/m² |
| 23°C | ISO 180/1A | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Metallized Haze Onset | 内部方法 | 204 | °C | |
| FMVSS Burning Speed | 2.00 mm | FMVSS 302 | 0 到 5 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.